+ | {| border="3" | ||
+ | |+ '''Silicon wafer table''' | ||
+ | |- style="background:orange; color:white" | ||
+ | ! Wafer ID !! Diameter (inches) !! Thickness (um) !! Orientation !! Dopant Species !! Resistivity (ohm-cm) !!# bought !! # remaining !! Supplier !! Note | ||
+ | |- | ||
+ | | n/a || 4 || 500 || 100 || As || 0.001 - 0.005 || 25 || 25 || University Wafer || CEEM - Si Nanowires | ||
+ | |- | ||
+ | | n/a || 3 || 380 || 111 || Sb || 0.019 - 0.025 || 20 || 20 || University Wafer || CEEM - Si Nanowires | ||
+ | |- | ||
|} | |} |
Revision as of 18:17, 29 July 2010
Wafer ID | Substrate(um) | BOX(um) | Device layer (um) | Doped Si | Undoped Si | # bought | # remaining | Supplier | Note |
---|---|---|---|---|---|---|---|---|---|
1I29437.1 | 675 | 1 | 0.7 | 0.2um 1E14 B | 0.5um 1E10 | 21 | 18 | SOITEC+LSRL | |
1I29437.1 | 675 | 1 | 0.4 | 0.2um 1E14 B | 0.2um 1E10 | 4 | 0 | SOITEC+LSRL | |
1H74447.1 | 675 | 1 | 0.7 | 0.3um 1E14 p type | 0.4um 1E10 | 10 | 2+1/3+1/3 | SOITEC | |
1H74447.1 | 675 | 1 | 0.6 | 0.3um 1E14 p type | 0.3um 1E10 | 5 | 3 | SOITEC | |
1H74447.1 | 675 | 1 | 0.55 | 0.3um 1E14 p type | 0.25um 1E10 | 10 | 3 | SOITEC | |
1G47090.1 | 675 | 1 | 1 | 0.3um 1E14 p type | 0.7um 1E10 | 10 | 2 | SOITEC | |
675 | 3 | 1 | 0.25um 1E14 p type | 0.75um 1E10 | 10 | 7+1/2+1/2 | SOITEC |
Wafer ID | Substrate(um) | BOX(um) | Device layer (um) | Details of device layer | Rib Etch (um) | # bought | # remaining | Supplier | Note |
---|---|---|---|---|---|---|---|---|---|
H4JYY8G | 1 | 0.7 | Undoped Si | 0.3 | 1 | 1/4 | umonyx/Intel | LASOR/PhASER | |
H4JYY8G | 1 | 0.7 | Undoped Si | 0.4 | 1 | 1 | umonyx/Intel | LASOR/PhASER | |
H4JYY8G | 1 | 0.7 | Undoped Si | 0.3 | 1 | 1 | umonyx/Intel | LASOR/PhASER, oxidation smooth | |
Wafer ID | PL(nm) | Data and spec-sheet | # bought | # remaining | Supplier | Note |
---|---|---|---|---|---|---|
GLDA0908271-C | 1545 | 5 | 3 | LandMark | LASOR/PhASER 200nm SCH with center QW | |
Wafer ID | Diameter (inches) | Thickness (um) | Orientation | Dopant Species | Resistivity (ohm-cm) | # bought | # remaining | Supplier | Note |
---|---|---|---|---|---|---|---|---|---|
n/a | 4 | 500 | 100 | As | 0.001 - 0.005 | 25 | 25 | University Wafer | CEEM - Si Nanowires |
n/a | 3 | 380 | 111 | Sb | 0.019 - 0.025 | 20 | 20 | University Wafer | CEEM - Si Nanowires |